Denver International Airport, CO, USA
N210GL
BEECH 1900D
During a post flight inspection the pilot discovered a hydraulic leak on the nose landing gear that was emanating from a crack in the nose landing gear end cap. The end cap was examined and found to have failed in fatigue that initiated from multiple origins at an internal diameter. The fatigue had propagated significantly into the wall thickness of the end cap and through the thickness at one location. The striation count revealed that the fatigue crack had initiated and been growing in the end cap for at least 15,305 cycles. The end cap had been inspected using an ultrasonic method recommended by the manufacturer 337 cycles prior to the incident. The crack was present at the time of the inspection which indicated that the inspection method was ineffective in detecting the crack. The timing of the end cap inspection was in compliance with the manufacturer’s recommendation. Examination of the microstructure of the material revealed that the longitudinal grain direction was oriented parallel to the shuttle valve bore in the end cap. Resistance to fatigue can be improved by aligning the principle tension stresses in the end cap with the longitudinal grain direction. It is probable that the manufacturer had determined that the grain direction was a contributing factor to fatigue failure in the end cap and revised the end cap drawing to require a grain direction along the longitudinal axis of the end cap in February 2010. No engineering data to support the drawing revision was made available.
HISTORY OF FLIGHT On February 17, 2012, about 0830 mountain standard time, the pilot of a Beechcraft 1900D airplane, N210GL, discovered a hydraulic leak on the nose landing gear (NLG) during a post flight inspection. The airplane was registered to Great Lakes Aviation and operated by Great Lakes Airlines as a 14 Code of Federal Regulations, Part 121 scheduled passenger flight. The airplane had just completed a flight from Laramie, Wyoming, to Denver, Colorado. DAMAGE TO AIRPLANE The pilot’s inspection of the NLG revealed a crack in the NLG actuator end cap, part number (P/N) 25703-4. The end cap, serial number (S/N) 524, was removed from the actuator and shipped to the NTSB. AIRCRAFT INFORMATION The NLG actuator was delivered new with the airplane and had accumulated 32,365.4 hours and 39,655 cycles since new. Great Lakes Airlines performed an ultrasonic inspection in accordance with the instructions in the Model 1900D Airliner Maintenance Manual 337 cycles prior to the incident. According to the operator, the NLG actuator had never been overhauled. TESTS AND RESEARCH The NLG end cap was examined in the National Transportation Safety Board (NTSB) Materials Laboratory. A visible crack extended circumferentially from the primary extend port on one side of the end cap, around the diameter of the end cap, to the secondary extend port on the other side. The intact portion of the end cap between the ports was cut toward the center line of the shuttle valve bore, and the two pieces were separated to examine the fracture faces. Examination of the fracture faces revealed a relatively flat, smooth zone and ratchet marks originating at the intersection of a radius with an inner diameter of the end cap, consistent with fatigue. The fatigue zone extended outwards almost uniformly through the wall thickness of the end cap, with a preference to the shuttle valve bore, and had propagated entirely through the thickness near the aft side (as installed with the landing gear extended) of the end cap. The fracture face outside of the fatigue zone displayed a rough, grainy surface consistent with an overload event. Samples were removed from the end cap and metallurgically mounted, polished, and etched in order to display the material microstructure at different orientations. The etchant revealed a longitudinal grain structure that was oriented parallel to the shuttle valve bore. The surface finish and machined radius were found to satisfy the drawing requirements. The fatigue zone was examined in the scanning electron microscope in order to assess and count the individual fatigue striations which are individual crack arrest features left on a fatigue fracture as a result of one load application. A location near the shuttle valve bore that contained the longest length of fatigue propagation was chosen to perform the count. Near the beginning of the crack it was determined that there were 29 individual striations in a measured crack length of 11.25 micrometers. Near the end of the crack it was determined that there were 19 individual striations in a measured length of 22.5 micrometers. It was then calculated that there were approximately 15,305 striations along the length of the crack propagation at this location. Since the full crack length could not be determined due to the fatigue zone propagating into the shuttle valve bore, the striation count is an approximate and minimum value. According to the Metals Handbook Desk Edition, 2nd Edition, 1998, wrought aluminum products such as the end cap generally exhibit differences in tensile properties and in resistance to fatigue stresses in the three orthogonal grain directions (longitudinal, long-transverse, and short-transverse) with the longitudinal direction being superior. Typically, fatigue loading in the longitudinal grain direction can provide a 5 to 10 percent improvement in fatigue strength according to the Metals Handbook, 8th Edition, Volume 1, 1961. The principal tensile stresses in the end cap are in the longitudinal direction and result from hydraulic pressure. ADDITIONAL INFORMATION The fatigue cracking evident on the NLG end cap is similar to cracking found on the end caps of three different Beechcraft 1900D airplanes operated by Great Lakes Airlines. The details are documented in NTSB investigations CEN11IA341, ENG12IA013, and ENG12IA024. As a result of some previous NLG end cap fractures and the preliminary findings from the CEN11IA341 investigation, Hawker Beechcraft instituted some changes to their recommended maintenance program for the NLG actuator. On August 1, 2010, the Model 1900D Airliner Maintenance Manual (AMM) was revised to add a recommended overhaul of the NLG assembly (including actuator) every 10,000 cycles or 5 years, whichever occurs first. This new requirement was to be complied with within 15 months after the August 1 revision. On May 1, 2011, a section was added to the AMM to include instructions for inspecting the NLG actuator end cap for cracks using an ultrasonic inspection method. Additionally, on May 1, 2011, the AMM was revised to add a recommended repetitive ultrasonic inspection of the NLG actuator every 1,200 cycles once the actuator had accumulated 8,000 cycles since new or newly overhauled. On November 1, 2011, a Temporary Revision to the AMM was released to change the NLG ultrasonic inspection time in order to deal with some supplier issues. If the actuator could not be overhauled or replaced by November 1, 2011, the revision allowed the actuator to remain in operation as long as the ultrasonic inspection had been performed within the last 1,200 cycles and recommended repeat ultrasonic inspections every 600 cycles. The end cap is produced according to the details of Airight, Inc. (now called APPH, Inc.) drawing 25703 which is currently at revision P. Revision N to the drawing was approved in February 2010 and added a specified longitudinal grain direction along the longitudinal axis of the end cap. Prior to this revision there was no requirement for a grain direction. According to APPH, the change was initiated by the supplier of the raw material through the purchasing department and had nothing to do with the fatigue failures of the end caps. No engineering data or other information was supplied to support the change. APPH also informed the NTSB that their standard practice was to stamp the actuator serial number in the recessed area between the ports on the end cap for every overhauled actuator since at least 2004. On February 13, 2013, the NTSB issued recommendations A-13-04, 05, and 06 to Hawker Beechcraft Corporation to address fatigue cracking of NLG end caps on Beechcraft 1900D airplanes.
A failure of the nose landing gear end cap due to fatigue. Contributing to the failure were the ineffective inspection and the unknown effect of grain direction on fatigue life.
Source: NTSB Aviation Accident Database
Aviation Accidents App
In-Depth Access to Aviation Accident Reports