Burlington, WA, USA
N5808U
PIPER PA-28-140
During the landing roll, the airplane began to veer right, and the pilot applied left rudder and left braking action to align the airplane with the runway; however, both actions were ineffective. The airplane departed the right side of the runway and impacted an airport sign and a ditch. Postaccident examination of the left rudder bar assembly found that it had failed due to a fatigue crack. A rusted brown oxidized area near the center of the crack and surface features consistent with slow-growth fatigue indicated that the crack had been growing incrementally over a period of years. A review of the manufacturer's periodic inspection checklist, maintenance manual, and Service Letter No. 671 indicated that the rudder bar assembly should be inspected every 100 hours specifically for cracks in the area where the airplane's rudder bar failed. If maintenance personnel had inspected the airplane in accordance with these documents, the crack likely would have been found and the accident prevented.
On June 4, 2013, at about 0930 Pacific daylight time, a Piper PA-28-140, N5808U, was substantially damaged when it struck an airport sign following a loss of directional control during landing roll at Skagit Regional Airport, Burlington, Washington. The private pilot, the sole occupant, was not injured. The pilot/owner was operating the airplane under the provisions of 14 Code of Federal Regulations Part 91. Visual meteorological conditions prevailed for the personal cross-country flight, which had originated from Friday Harbor, Washington, approximately 20 minutes before the accident. A flight plan had not been filed. The pilot said that while on landing roll, he applied left rudder to straighten the airplane, with no response. He said he attempted to correct the right veering tendency with left braking action, and that was ineffective as well. The airplane departed the right side of the runway and impacted an airport sign and a ditch, which damaged the right wing. Postexamination of the left rudder control bar found that it had failed. Examination of the rudder control bar at the NTSB Materials Laboratory found a fatigue crack, which originated from the edge of a weld. There was a rusted brown oxidized area near the middle of the crack, and the surface of this area had topography and crack patterns consistent with slow growth fatigue progressing from the exterior surface radially through the tube wall. The airplane was manufactured in 1970, and according to the owner, it had an airframe total time of 3,479 hours when the accident occurred. The most recent annual inspection was completed on May 25, 2013. A review of the Piper Aircraft's periodic inspection checklist, maintenance manual, and Service Letter No. 671 dated October 5, 1973, indicated that the rudder bar assembly should be inspected every 100 hours specifically for cracks in the area where the airplane's rudder bar failed. Further, the Service Letter stated that these periodic inspections could be discontinued if two reinforcement doublers were fabricated and welded to the rudder bar in the affected area. There were no reinforcement doublers on the airplane's rudder bar.
The failure of the rudder bar assembly during landing due to a fatigue crack. Contributing to the accident was the failure of maintenance personnel to perform an adequate inspection of the rudder bar assembly.
Source: NTSB Aviation Accident Database
Aviation Accidents App
In-Depth Access to Aviation Accident Reports